Impregnation mode in wood plastic composite
Abstract
Bulk monomer MMA was impregnated into simul, a fuel wood of Bangladesh, under vacuum and under normal temperature and pressure conditions in order to compare the mode of impregnation and its effect on various characteristic parameters of wood plastic composites. Methanol (MeOH) was used as the swelling solvent with methylmethacrylate (MMA) at MMA: MeOH = 70:30, v/v. Impregnation of the bulk monomer was very high under vacuum compared to that at normal condition; but the difference of grafting of MMA to the wood cellulose under these two impregnating conditions was much lower as compared to that of the uptakes of impregnating solution MMA + MeOH under these two modes of impregnation. Incorporation of additives to MMA + MeOH has substantially enhanced grafting, tensile strength, bending strength and compression strength of the composite to such an extent that there is virtually very little difference between vacuum impregnation and normal impregnation. Considering the available data it is suggested that the impregnation under normal condition is preferable because different substrates of various sizes and shapes can be suitably impregnated under normal condition while vacuum impregnation has several limitations in this respect.
Publication Title
Radiation Physics and Chemistry
Recommended Citation
Husain, M., Khan, M., Ali, M., Ali, K., & Mustafa, A. (1996). Impregnation mode in wood plastic composite. Radiation Physics and Chemistry (6), 781-786. https://doi.org/10.1016/S0969-806X(96)00137-5